Brazing Guide

by Dr. Girish Dahake, Sr. Vice President, Worldwide Applications

While brazing with induction heating, the importance of cleanliness, degreasing as well as the removal of any oxide films on the surface of the parts can not be over-stressed. The surface finish affects the flow of the brazing material; a rough, corroded surface will result in globs of braze alloy throughout the joint area.
Brazing Overview

Precision Induction Heating

Precision Induction Heating

Read our 4-page brochure "About Induction Heating". Learn more about how the science of induction technology can solve your precision heating problems.

Induction Work Coils

Induction Work Coils

The work coil is the component in the induction heating system that defines how effective and how efficiently your work piece is heated. Read our brochure 'Induction Work Coils' explaining the fundamentals of the induction work coil


A good fit assists in heat conduction between parts and helps to prevent overheating. It also requires less brazing material for the joint. Typical joint clearances range from 2-5 thousandths of an inch for good braze joints.

brazing steel to brass

The brazing operation should be such that the parts to be joined are heated uniformly at the joint areas. Induction heating coils should be arranged so that maximum energy is directed towards the heaviest mass, when brazing a thick and heavy part to a small thin part.

brazing steel to steel

Differential expansion between two dissimilar materials being joined can sometimes introduce difficulties. This particularly applies when a brass part is fitted inside a steel part. During the cooling cycle brass contracts away from the steel and causes cracks in the braze joint. The same effect can occur between steel and tungsten carbides - a common material combination in cutting tool industry.

brazing brass to brass

The work coil needs to be designed to deliver uniform heat to both the outer and the inner tubes in order to ensure that the outer tube does not expand and move away from the inside tube.

Alloy Position
protective atmosphere brazing

Silver brazing alloys are extremely fluid above 650°C and tend to flow in the direction from which heat is applied. Whenever using braze rings they should be positioned either partly or wholly in a chamfered recess so that they are shielded from direct induction heating. There is also a danger of the braze alloy melting before the joint reaches brazing temperature. The alloy should be in form of an open ring, which is more difficult to heat with induction than a complete loop. The ring should also be a tight fit to the part, and if necessary flattened to increase the surface area in contact. Sometimes it is recommended to use two rings of a much smaller wire than one ring of a larger wire diameter.


The power setting and the exact heating time are normally determined experimentally. Once established for a particular component, they will produce consistent good parts without requiring external temperature control. It is usually preferred to heat several parts simultaneously to achieve a given production rate than try to reduce the cycle time for one part.


When considering the production rate required, emphasis is often placed on the heating time while the cooling time is often ignored. This may be justified for a good number of applications; however, larger components require cooling time as much as if not more than the heating time. Cooling time can be reduced by the use of compressed air, etc.